Fast Curing Double Component Industrial Adhesive Glue / Fiberglass Adhesive Glue

Fast Curing Double Component Industrial Adhesive Glue / Fiberglass Adhesive Glue

Fast Curing Double Component Industrial Adhesive Glue / Fiberglass Adhesive Glue This fast curing double component adhesive ( construction silicone/window glass silicone/silicone rubber/silicone sealant/silicone adhesive ) Used in metal, ceramic, cement, wood, ABS, PU, glass and Fiber glass...

Send Inquiry
Product Details

Fast Curing Double Component Industrial Adhesive Glue / Fiberglass Adhesive Glue

 

A Component: Polyhydric Alcohols B Component: Isocyanate
Viscosity: B Component (3# Rotor20rpm): 2000 2000±1000 MPa.s Density(g/cm3): B Component:1.2±0.1g/cm3
Pot Life(min): >4 Surface Drying Time(23±2℃): 4~10 Min

 

This fast curing double component adhesive (construction silicone/window glass silicone/silicone rubber/silicone sealant/silicone adhesive) Used in metal, ceramic, cement, wood, ABS, PU, glass and Fiber glass

Product specificationTechnical Data Sheet

8664 Fast curing double component adhesive

Curing fast, high bond strength, strength rises rapidly; environmental friendly, water resistance, low temperature resistance No mildew, non-toxic, non-corrosive, excellent impact resistance and durability. Use to replace the greatSmells, not environmentally friendly two-component acrylic adhesive.

Typical usage

Used in metal, ceramic, cement, wood, ABS, PU, glass and

Fiber glass and other materials, or mutual self-stick.

Characteristics before curing

Typical value range

Appearance

A component Gray to pale yellow paste

B component Light brown liquid

 

Base material chemical composition

A component polyhydric alcohols

B component Isocyanate

viscosity(mPa.s)

(GB/T2794-1995) Brookfield RVF

A component

(6# rotor50rpm): 9000 9000±3000mPa.s

B component

(3# rotor20rpm): 2000 2000±1000 mPa.s

density(g/cm3)

(GB/T13354-1992) 1.3 A component:1.3±0.1g/cm3

1.2 B component:1.2±0.1g/cm3

pot life(min) >4

surface drying time(23±2℃) 6 4~10 min

 

After curing characteristics

Shear strength (Mpa)

23±2℃solidifytime 2h

(Al/Al) 7.0 ≥5

23±2℃solidify time7 days

(Al/Al) 11.5 ≥10

Working temperature(℃) -40-90

 

Using direction:

 

·Clean the surface to be bonded to be clean, dry;

·With glue visua

A:B

volume ratio1:1,Rapid mixing,A:B = 1:1 (V/V)

Accurate calibration scale= 1.1:1(W/W);

·Sizingtrial period is completed, the contact pressure is applied

·Room temperature curing or heat curing Curing

 

Noted:

·sizing ambient temperature 0 ~ 35 ℃, humidity <70%; unused glue should be closed immediately

store seal to prevent moisture absorption; highly contaminated glue cannot reload into the original packaging bucket

·keep away from children

·This product contains isocyanates substances which has the irritationon the skin andeyes. Recommended for use in a well-ventilated place

·In case of contact with eyes and skin, immediately rinse with water

·Product safety information, please refer to the product MSDS

 

Package:

 

Ordering Code: A component:8664A4,4.4kg/bucket,4 bucket/box

B component:8664B4,4kg/bucket,4 bucket/box

 

Storage conditions

Store in a cool dry place 8-28 ℃

Storage period: 12 months

 

Special version

The data in this manual were obtained under laboratory conditions, the use of environmental differences, the user data and make reference to these

Conditions for analysis and testing.Huitian does not guarantee sales of our productsand use of the product and the specific conditions problem with the product.

We are not liable for any direct, indirect or incidental damages. Users in the course of any problems, you can return to Huitiantechnology and Service department, we will provide you with all the help.

Hot Tags: fast curing double component industrial adhesive glue / fiberglass adhesive glue, China, manufacturers, suppliers, factory, price, buy, high quality, made in China
Related Products
Inquiry